PREPARATION AND CHARACTERIZATION OF Li1.4Al0.4Ti1.6(PO4)3 CONDUCTING ELECTROLYTE

Authors

  • Maziidah Hamidi Faculty of Applied Sciences, Universiti Teknologi MARA, 40000 Shah Alam, Selangor, Malaysia Author
  • Syafawati Nadiah Mohamed Faculty of Applied Sciences, Universiti Teknologi MARA, 40000 Shah Alam, Selangor, Malaysia Author
  • Muhd Zu Azhan Yahya Faculty of Applied Sciences, Universiti Teknologi MARA, 40000 Shah Alam, Selangor, Malaysia Author

Keywords:

LATP, sol-gel method, EIS, XRD, FESEM

Abstract

The Li1.4Al0.4Ti1.6(PO4)3 glass ceramic with NASICON-type phase has been synthesized. Ionic conductivity identification of the pelletized powder was carried out by electrochemical impedance spectrometer (EIS). The highest ionic conductivity obtained for Li1.4Al0.4Ti1.6(PO4)3 is 1.22x10-5 S cm-1 after being annealed at 800ºC for 3 hours in air.

Downloads

Published

10-05-2026

Issue

Vol. 20 No. (1&2) (2012): Solid State Science and Technology

Section

Articles

License

Creative Commons License

This work is licensed under a Creative Commons Attribution 4.0 International License.